_aToF-SIMS study of oxide films thermally grown on nickel-base alloys _cX. Wu, S. Voyshnis, A. Seyeux [et al.] |
| 520 | 3 | _aThe oxidation behaviours of polycrystalline and monocrystalline Ni-base alloys (Ni-16Cr-8Fe (wt%)) were investigated in situ by Time-of-Flight Secondary Ion Mass Spectrometry (ToF-SIMS). The oxide layer formed is duplex: an inner chromium-rich layer and an outer layer which is rich in nickel and iron. Time evolution of the composition of inner layer from pure Cr2O3 towards spinel (NiCr2O4) was observed. The oxidation kinetics was accelerated by alloy grain boundaries, which can favour the diffusion of chromium. Both the parabolic and volatilization constants increased with increasing temperature, with kp varying from 1.9×10−3 to 1.6×10−2 nm2.s−1, and kv from 1.0×10−3 to 2.9×10−3 nm.s−1. | |
| 653 | _aоксидные пленки | ||
| 653 | _aсплавы на основе никеля | ||
| 653 | _aкинетика окисления | ||
| 655 | 4 |
_aстатьи в журналах _9745982 |
|
| 700 | 1 |
_aVoyshnis, Svetlana _9493064 |
|
| 700 | 1 |
_aSeyeux, Antoine _9493065 |
|
| 700 | 1 |
_aChumlyakov, Yuri I. _9100866 |
|
| 700 | 1 |
_aMarcus, Philippe _9493066 |
|
| 700 | 1 |
_aWu, Xiaocui _9493067 |
|
| 773 | 0 |
_tCorrosion science _d2018 _gVol. 141. P. 175-181 _x0010-938X |
|
| 852 | 4 | _aRU-ToGU | |
| 856 | 4 | _uhttp://vital.lib.tsu.ru/vital/access/manager/Repository/vtls:000653360 | |
| 908 | _aстатья | ||
| 999 | _c451265 | ||