_aEffects of crystallographic orientation on the superelastic response of FeMnAlNi single crystals _cL. W. Tseng, J. Ma, S. J. Wang [et.al.] |
| 504 | _aБиблиогр.: 30 назв. | ||
| 520 | 3 | _aThe effects of crystal orientation on the tensile superelastic response of the Fe43.5Mn34Al15Ni7.5 single crystalline shape memory alloy, oriented along the < 100 > and < 123 > directions were investigated. The single crystals aged at 200 °C for 3 h demonstrated superelastic strains of 3.6% along the < 100 > orientation and 7.8% along the < 123 > orientation. Although the theoretical transformation strain in the < 100 > orientation is higher than that in the < 123 > orientation, the < 123 > oriented single crystals demonstrate better superelastic recovery in tension due to a higher number of active martensite variants, which promote better accommodation of internal strains and help minimize defect formation during transformation. | |
| 653 | _aсверхэластичность | ||
| 653 | _aэффект памяти формы | ||
| 653 | _aмонокристаллы | ||
| 653 | _aсплавы | ||
| 655 | 4 |
_aстатьи в журналах _9745982 |
|
| 700 | 1 |
_aTseng, L. W. _9262794 |
|
| 700 | 1 |
_aWang, S. J. _9262795 |
|
| 700 | 1 |
_aKaraman, Ibrahim _9100868 |
|
| 700 | 1 |
_aChumlyakov, Yuri I. _9100866 |
|
| 700 | 1 |
_aMa, Ji _9147063 |
|
| 773 | 0 |
_tScripta materialia _d2016 _gVol. 116. P. 147-151 _x1359-6462 |
|
| 852 | 4 | _aRU-ToGU | |
| 856 | 7 | _uhttp://vital.lib.tsu.ru/vital/access/manager/Repository/vtls:000621840 | |
| 908 | _aстатья | ||
| 999 | _c428586 | ||