Study of highly defective titanium dioxide prepared via pulsed laser ablation Z. P. Fedorovich, E. D. Fakhrutdinova, M. A. Gerasimova, V. A. Svetlichnyi
Material type: ArticleContent type: Текст Media type: электронный Subject(s): импульсная лазерная абляция | диоксид титанаGenre/Form: статьи в сборниках Online resources: Click here to access online In: 6th International conference on advanced nanoparticle generation & excitation by lasers in liquids (ANGEL2021), Hefei, China, June 16th-18th, 2021 : program & technical digest P. 86Abstract: TiO2 powder was synthesized in the following way. At first, a colloidal solution of Ti in distilled water was obtained by PLA using Nd:YAG laser (wavelength of 1064 nm, frequency of 20 Hz, pulse duration of 7 ns). Then the colloidal solution was dried at 60 °C. After that, the powder was annealed at different temperatures.Библиогр.: 3 назв.
TiO2 powder was synthesized in the following way. At first, a colloidal solution of Ti in distilled water was obtained by PLA using Nd:YAG laser (wavelength of 1064 nm, frequency of 20 Hz, pulse duration of 7 ns). Then the colloidal solution was dried at 60 °C. After that, the powder was annealed at different temperatures.
There are no comments on this title.